Organic anti-reflective coating polymer, anti-reflective coating composition comprising the same and method of preparation thereof

ABSTRACT

An organic anti-reflective polymer having the following Formula 1, its preparation method, an anti-reflective coating composition comprising the said organic anti-reflective polymer and a preparation method of an anti-reflective coating made therefrom. The anti-reflective coating comprising the disclosed polymer eliminates standing waves caused by the optical properties of lower layers on the wafer and by the thickness changes of the photoresist, prevents back reflection and CD alteration caused by the diffracted and reflected light from such lower layers. Such advantages enable the formation of stable ultrafine patterns suitable for 64M, 256M, 1G, 4G, and 16G DRAM semiconductor devices and improve the production yields. Further, it is also possible to control the k value and the increased hydrophobicity facilitates EBR (Edge Bead Removal).

BACKGROUND

[0001] 1. Technical Field

[0002] An organic anti-reflective polymer and its preparation method are disclosed which prevents back reflection of lower film layers and eliminates standing wave that occurs as a result of thickness changes of the photoresist and light, in a process for fabricating ultrafine patterns that use photoresist for lithography by using 248 nm KrF and 193 nm ArF. More particularly, the disclosed organic anti-reflective polymer is useful for fabricating ultrafine patterns of 64M, 256M, 1G, and 4G DRAM semiconductor devices. A composition containing such organic anti-reflective polymer, an anti-reflective coating layer made therefrom and a preparation method thereof is also disclosed.

[0003] 2. Description of the Background Art

[0004] In a fabrication process of ultrafine patterns for preparing semiconductor devices, standing waves and reflective notching inevitably occur due to the optical properties of lower film layer on the wafer and due to the thickness changes in the photosensitive film. In addition, there is another problem in that a CD (critical dimension) alteration is caused by diffracted and reflected light from the lower film layers. Thus, it has been suggested to introduce anti-reflective coating that prevents back reflection at a lower film layer by introducing organic material with high absorbance at a wavelength range of the light employed as a light source.

[0005] Anti-reflective coatings are classified into inorganic and organic anti-reflective coatings depending upon the material used, or into absorptive and interfering anti-reflective coatings based on the operation mechanism. For microlithography using I-line (365 nm wavelength) radiation, inorganic anti-reflective coatings are predominantly used, while TiN and amorphous carbon is employed as an absorptive system and SiON is employed as an as interfering system.

[0006] In a fabrication process of ultrafine patterns using KrF laser, SiON has been mainly used as an inorganic anti-reflective film. However, in the case of an inorganic anti-reflective film, no material has been known which enables the control of the interference at 193 nm, the wavelength of the light source. Thus, there has been great deal of efforts to employ an organic compound as an anti-reflective coating.

[0007] To be a good organic anti-reflective coating, the following conditions must be satisfied. First, peeling of the photoresist layer due to the dissolution in a solvent must not take place when conducting a lithographic process. In order to achieve this goal, a molded coating must be designed to form a cross-linked structure without producing any chemical by-product. Second, chemicals such as acid or amine must not come-in or go-out from the anti-reflective coating. This is because when acid migrates from anti-reflective coating, undercutting occurs at a lower part of the pattern while footing may occur when a base such as amine migrates. Third, the etching speed of the anti-reflective coating should be faster than the etching of the upper photosensitive film so as to facilitate etching process by using photosensitive film as a mask. Finally, the anti-reflective coating must be as thin as possible to an extent to sufficiently play a role as an anti-reflective coating.

[0008] The existing organic anti-reflective material are mainly divided into two types: (1) polymers containing a chromophore, cross-linking agent (single molecule) that cross-link the polymers and an additive (thermally variable oxidant); and (2) polymers which can cross link themselves and contain a chromophore and an additive (thermally variable oxidant). But these two types of anti-reflective material are problematic in that the control of k value is almost impossible because the content of the chromophore is defined according to the ratio as originally designed at the time of polymerization. Thus, if it is desired to change the k value, the polymer must be resynthesized.

SUMMARY OF THE DISCLOSURE

[0009] A novel organic polymer for anti-reflective coating and its preparation method are disclosed.

[0010] An anti-reflective coating composition comprising the aforementioned polymer and a preparation method thereof are also disclosed.

[0011] A semiconductor device on which a pattern is formed from such an anti-reflective coating by submicrolithography is also disclosed.

DETAILED DESCRIPTION OF THE PRESENTLY PREFERRED EMBODIMENTS

[0012] The following compounds having Formulas 1 and 2, respectively are provided which can be used in an anti-reflective coating.

[0013] The polymer of the above-structured Formula 1 is synthesized from the compound of the following Formula 10.

[0014] In the above Formulas 1 to 3:

[0015] R^(a) to R^(d) are each independently hydrogen or methyl;

[0016] R^(a) to R^(d), and R₁ to R₉ are each independently —H, —OH, —OCOCH₃, —COOH, —CH₂OH, or substituted or unsubstituted, or straight or branched alkyl or alkoxy alkyl having 1 to 5 carbon atoms;

[0017] 1, m and n each represents an integer selected from 1, 2, 3, 4 and 5;

[0018] w, x, y, and z each represents mole fraction from 0.01 to 0.99;

[0019] R₁₀ and R₁₁ are each independently straight or branched substituted C₁₋₁₀ alkoxy; and

[0020] R₁₂ is hydrogen or methyl.

[0021] The compound of Formula 2 is prepared by polymerizing (meth)acrolein to obtain poly(meth)acrolein followed by reacting the obtained polymeric product with branched or straight substituted alkyl alcohol having 1 to 10 carbon atoms.

[0022] In detail, (meth)acrolein is first dissolved in an organic solvent and added thereto a polymerization initiator to carry out polymerization under vacuum at a temperature ranging from about 60 to about 70° C. for a time period ranging from about 4 to about 6 hours. Then, the obtained polymeric product is reacted with branched or straight substituted alkyl alcohol having 1 to 10 carbon atoms in the presence of trifluoromethylsulfonic acid as a catalyst at a room temperature for a time period ranging from about 20 to about 30 hours.

[0023] In the above process, suitable organic solvent is selected from the group consisting of tetrahydrofuran (THF), cyclohexanone, dimethylformamide, dimethylsulfoxide, dioxane, methylethylketone, benzene, toluene, xylene and mixtures thereof. As a polymerization initiator, it can be mentioned 2,2-azobisisobutyronitrile (AIBN), benzoylperoxide, acetylperoxide, laurylperoxide, t-butylperacetate, t-butylhydroperoxide or di-t-butylperoxide. A preferred example of the said alkyl alcohol having 1 to 10 carbon atoms is ethanol or methanol.

[0024] A preferred compound of Formula 2 is selected from the group consisting of the compounds of the following Formulas 3 to 6.

[0025] The above compounds of Formulas 3 to 6 are readily cured in the presence of acid and other polymers having alcohol group.

[0026] The polymer of Formula 1 is prepared by reacting 9-anthracene methyliminealkylacrylate monomer, hydroxyalkylacrylate monomer, glycidylalkylacrylate monomer and methylmethacrylate monomer in an organic solvent and then polymerizing the obtained compound with a polymerization initiator. Any conventional organic solvent can be used in this process but a preferred solvent is selected from the group consisting of tetrahydrofuran, toluene, benzene, methylethylketone, dioxane and mixtures thereof. As a polymerization initiator, any conventional radical polymerization initiator can be used but it is preferred to use a compound selected from the group consisting of 2,2′-azobisisobutyronitrile, acetylperoxide, laurylperoxide, and t-butylperoxide. The above polymerization reaction is preferably carried out at a temperature ranging from about 50 to about 90° C. and the mole ratio of each monomer falls within the broad range, 0.01 to 0.99:0.01 to 0.99.

[0027] An anti-reflective coating composition can comprise a polymer of Formula 1 and a polymer of Formula 2.

[0028] Further, an anti-reflective coating composition can comprise a polymer of Formula 1, a compound of Formula 2 and an anthracene derivative as an additive. Illustrative, non-limiting examples of the anthracene derivatives (hereinafter, “anthracene derivative additive”) is selected from the group consisting of anthracene, 9-anthracenemethanol, 9-anthracenecarbonitrile, 9-antracene carboxylic acid, ditranol, 1,2,10-anthracentriol, anthraflavonic acid, 9-anthraldehydeoxime, 9-anthraldehyde, 2-amino-7-methyl-5-oxo-5H-[1]benzo-pyrano[2,3-b]pyridine-3-carbonitrile, 1-aminoanthraquinone, anthraquinone-2-carboxylic acid, 1,5-dihydroxyanthraquinone, anthrone, 9-anthryle trifluoro-methylketone, 9-alkylanthracene derivatives of the following Formula 7, 9-carboxylanthracene derivatives of the following Formula 8, 1-carboxylanthracene derivatives of the following Formula 9, and mixtures thereof.

[0029] wherein, R₁ to R₅ are —OH, —CH, —CH₂OH or substituted or unsubstituted, straight or branched alkyl or alkoxyalkyl having 1 to 5 carbon atoms.

[0030] A preparation method of an organic anti-reflective coating comprises the steps of dissolving a polymer of Formula 1 and a compound of Formula 2 in an organic solvent, filtering the obtained solution alone or in combination with at least one anthracene derivative additive as aforementioned, coating the filtrate on a lower layer and hard-baking the coated layer. More particularly, an example of the organic solvent used in this procedure includes ethyl 3-ethoxypropionate, methyl 3-methoxypropionate, cyclohexanone, and propyleneglycolmethylether acetate. It is preferred that the aforementioned solvent is used in an amount ranging from about 200 to about 5,000 wt.% based on the total weight of the anti-reflective coating resin used. The preferred temperature range for hard-baking rangines from about 100 to about 300° C.

[0031] An improved semiconductor device can be prepared from any of the aforementioned anti-reflective coating compositions.

[0032] A monomer having a large sized chromophore was first synthesized to enable for a polymer made therefrom to achieve a high absorbance at the wavelength of 248 nm. Further, in order to allow improved properties to a produced organic anti-reflective coating, such as good molding property, air-tightness, and dissolution resistance, an epoxy group was introduced to raise a cross linking reaction during a hard-baking step following a coating step. The obtained polymer is referred to as a primary polymer (the compound of Formula 1). In addition, a secondary polymer (the compound of Formula 2), a compound capable of forming a cross linkage upon the reaction with an alcohol group in resin was also synthesized to form a cross-linked product with the primary polymer by a thermal reaction. Further, a methacrylate group was also introduced into the primary polymer in order to make it more hydrophobic to facilitate EBR (Edge Bead Removal).

[0033] In particular, the cross-linking agents used are in the form of a polymer are designed to maximize the efficiency of the cross-linking reaction. Especially, it is possible to freely adjust the k value of the anti-reflective film by controlling the proportion of the primary polymer,

[0034] Further, the anti-reflective coating resin has a good solubility in all of the hydrocarbon solvents while has a dissolution resistance in any of the solvents during a hard-baking step. In addition, no undercutting or footing is experienced in the fabrication process of patterns. Especially, because the anti-reflective coating resin of the present invention is made from acrylate polymer which enables higher etching speed relative to that of the photosensitive film during etching process, the etching selectivity is improved.

[0035] The following examples are set forth to illustrate more clearly the disclosed principles and disclosed practices to a person skilled in the art. As such, they are not intended to limit the disclosure, but are illustrative of certain preferred embodiments.

EXAMPLES Example 1 Preparation of poly[9-anthracenemethylimineethylacrylate-(2-hydroxyethylacrylate)-glycidylmethacrylate-methylmethacrylate]

[0036] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylacrylate monomer/0.3 mole of 2-hydroxyethylacrylate/0.2 mole of glycidylmethacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethyl-imineethylacrylate-(2-hydroxyethylacrylate)-glycidylmethacrylate-methylmeth-acrylate] resin of the following Formula 11 (yield: 80%).

Example 2 Preparation of poly[9-anthracenemethylimineethylacrylate-(3-hydroxypropylacrylate)-glycidylmethacrylate-methylmethacrylate]

[0037] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylacrylate monomer/0.3 mole of 3-hydroxypropylacrylate/0.2 mole of glycidylmethacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethyl-imineethylacrylate-(3-hydroxypropylacrylate)-glycidylmethacrylate-methylmeth-acrylate] resin of the following Formula 12 (yield: 79%).

Example 3 Preparation of poly[9-anthracenemethylimineethylacrylate-(2-hydroxyethylacrylate)-glycidylacrylate-methylmethacgrylate]

[0038] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylacrylate monomer/0.3 mole of 2-hydroxyethylacrylate/0.2 mole of glycidylacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethyl-imineethylacrylate-(2-hydroxyethylacrylate)-glycidylacrylate-methylmethacrylate] resin of the following Formula 13 (yield: 81%).

Example 4 Preparation of poly[9-anthracenemethylimineethylacrylate-(3-hydroxypropylacrylate)-glycidylacrylate-methylmethacrylate]

[0039] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylacrylate monomer/0.3 mole of 3-hydroxypropylacrylate/0.2 mole of glycidylacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[⁹-anthracenemethyl-imineethylacrylate-(3-hydroxypropylacrylate)-glycidylacrylate-methylmeth-acrylate] resin of the following Formula 14 (yield: 79%).

Example 5 Preparation of poly[9-anthracenemethylimineethylacrylate-(4-hydroxybutylacrylate)-glycidylacrylate-methylmethacrylate]

[0040] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylacrylate monomer /0.3 mole of 4-hydroxybutylacrylate/0.2 mole of glycidylacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethylimineethylacrylate-(4-hydroxybutylacrylate)-glycidylacrylate-methylmethacrylate] resin of the following Formula 15 (yield: 80%).

Example 6 Preparation of poly[9-anthracenemethylimineethylmethacrylate-(2-hydroxyethylacrylate)-glycidylmethacrylate-methylmethacrylate]

[0041] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylmethacrylate monomer/0.3 mole of 2-hydroxyethylacrylate/0.2 mole of glycidylmethacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethyl-imineethylmethacrylate-(2-hydroxyethylacrylate)-glycidylmethacrylate-methyl-methacrylate] resin of the following Formula 16 (yield: 80%).

Example 7 Preparation of poly[9-anthracenemethylimineethylmethacrylate-(3-hydroxypropylacrylate)-glycidylmethacrylate-methylmethacrylate]

[0042] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylmethacrylate monomer/0.3 mole of 3-hydroxypropylacrylate/0.2 mole of glycidylmethacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethyl-imineethylmethacrylate-(3-hydroxypropylacrylate)-glycidylmethacrylate-methyl-methacrylate] resin of the following Formula 17 (yield: 78%).

Example 8 Preparation of poly[9-anthracenemethylimineethylmethacrylate-(4-hydroxybutylacrylate)-glycidylmethacrylate-methylmethacrylate]

[0043] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylmethacrylate monomer/0.3 mole of 4-hydroxybutylacrylate/0.2 mole of glycidylmethacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracene-methylimineethylmethacrylate-(4-hydroxybutylacrylate)-glycidylmethacrylate-methylmethacrylate] resin of the following Formula 18 (yield: 81%).

Example 9 Preparation of poly[9-anthracenemethylimineethylmethacrylate-(2-hydroxyethylacrylate)-glycidylacrylate-methylmethacrylate]

[0044] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylmethacrylate monomer/0.3 mole of 2-hydroxyethylacrylate/0.2 mole of glycidylacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethyl-imineethylmethacrylate-(2-hydroxyethylacrylate)-glycidylacrylate-methylmeth-acrylate] resin of the following Formula 19 (yield: 79%).

Example 10 Preparation of poly[F9-anthracenemethylimineethylmethacrylate-(3-hydroxypropylacrylate)-glylycidylacrylate-methylmethacrylate]

[0045] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylmethacrylate monomer/0.3 mole of 3-hydroxypropylacrylate/0.2 mole of glycidylacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethyl-imineethylmethacrylate-(3-hydroxypropylacrylate)-glycidylacrylate-methylmeth-acrylate] resin of the following Formula 20 (yield: 81%).

Example 11 Preparation of poly[9-anthracenemethylimineethylmethacrylate-(4-hydroxybutylacrylate)-glycidylacrylate-methylmethacrylate]

[0046] A 500 ml round bottom flask was charged with 0.3 mole of 9-anthracenemethylimineethylmethacrylate monomer/0.3 mole of 4-hydroxybutylacrylate/0.2 mole of glycidylacrylate/0.2 mole of methylmethacrylate while stirring and 300 g of separately prepared tetrahydrofuran was added to a complete mixture. Thereafter, from about 0.1 to about 3.0 g of 2,2′-azobisisobutyronitrile was added to allow a polymerization reaction at a temperature ranging from about 60 to about 75° C. under a nitrogen atmosphere for a time period ranging from about 5 to about 20 hours. After the completion of the reaction, the obtained solution was precipitated with ethyl ether or n-hexane solvent and then filtered and dried to obtain poly[9-anthracenemethyl-imineethylmethacrylate-(4-hydroxybutylacrylate)-glycidylacrylate-methylmeth-acrylate] resin of the following Formula 21 (yield: 80%).

Example 12 Preparation of an anti-reflective coating solution

[0047] A polymer of Formula 1 as prepared in one of Examples 1 to 11 and a polymer of Formula 2 were dissolved in propyleneglycolmethylether acetate. The obtained solution, alone or in combination with about 0.1 to about 0 wt. % of at least one anthracene derivative additive to complete dissolution, was filtered, coated on a wafer, and hard-baked at a temperature ranging from about 100 to about 300° C. for a time period ranging from about 10 to about 1,000 seconds. Then, a photosensitive film was applied thereon and followed by a routine ultrafine pattern fabrication process.

[0048] The cross-linking agent used is in a form of a polymer is designed to maximize the cross-linking efficiency. Further, it is possible to freely modify the k value of an organic anti-reflective coating by controlling the proportion of a primary polymer. Thus, the prior art problem wherein the control of the k value was not possible has been overcome.

[0049] Moreover, the disclosed anti-reflective coating resin includes a monomer having a large sized chromophore that enables a polymer made therefrom to achieve a high absorbance at the wavelength of 248 nm. The disclosed anti-reflective coating resin also includes an epoxy group which enables a cross-linkage. Further, by introducing a methacrylate group into a primary polymer thereof, its hydrophobicity is increased which in turn facilitates EBR (Edge Bead Removal).

[0050] Further, the disclosed anti-reflective coating resin dissolves well in all hydrocarbon solvent, while does not dissolve in any of the solvents during a hard-baking step and it does not experience undercutting and footing in a fabrication process of patterns. Particularly, because the disclosed anti-reflective coating resin of the present invention is composed of acrylate polymer, its etching speed is higher than that of a photosensitive film and thus, the etching selectivity can be improved.

[0051] The present invention has been described in an illustrative manner, and it is to be understood the terminology used is intended to be in the nature of description rather than of limitation. It must be understood that many modifications and variations of the present invention are possible in light of the above teachings. Therefore, it is to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described. 

What is claimed is:
 1. A compound having the structure of the following Formula 1:

wherein: R^(a) to R^(d) are each independently hydrogen or methyl; R_(a) to R_(d), and R₁ to R₉ are each independently selected from the group consisting of —H, —OH, —OCOCH₃, —COOH, —CH₂OH, alkyl having 1 to 5 carbon atoms and alkoxy alkyl having 1 to 5 carbon atoms; l, m and n each represent an integer selected from the group consisting of 1, 2, 3, 4 and 5; w, x, y, and z each represent a mole fraction ranging from about 0.01 to about 0.99;
 2. The compound of claim 1 which is poly[9-anthracenemethylimineethylacrylate-(2-hydroxyethylacrylate)-glycidylmethacrylate-methylmethacrylate], wherein R^(a) and R^(b) are each hydrogen, R^(c) and R^(d) are each methyl, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 2 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively
 3. The compound of claim 1 which is poly[9-anthracenemethylimineethylacrylate-(3-hydroxypropylacrylate)-glycidylmethacrylate-methylmethacrylate], wherein R^(a) and R^(b) are each hydrogen, R^(c) and R^(d) are each methyl, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 3 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively
 4. The compound of claim 1 which is poly[9-anthracenemethylimineethylacrylate-(2-hydroxyethylacrylate)-glycidylacrylate-methylmethacrylate], wherein R^(a), R^(b) and R^(c) are each hydrogen, R^(d) is methyl, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 2 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 5. The compound of claim 1 which is poly[9-anthracenemethylimineethylacrylate-(3-hydroxypropylacrylate)-glycidylacrylate-methylmethacrylate], wherein R^(a), R^(b) and R^(c) are each hydrogen, R^(d) is methyl, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 3 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 6. The compound of claim 1 which is poly[9-anthracenemethylimineethylacrylate-(4-hydroxybutylacrylate)-glycidylacrylate-methylmethacrylate], wherein R^(a), R^(b) and R^(c) are each hydrogen, R_(d) is methyl, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 4 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 7. The compound of claim 1 which is poly[9-anthracenemethylimineethylmethacrylate-(2-hydroxyethylacrylate)-glycidylmethacrylate-methylmethacrylate], wherein R^(a), R^(c) and R^(d) are each methyl, R^(b) is hydrogen, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 2 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 8. The compound of claim 1 which is poly[9-anthracenemethylimineethylmethacrylate-(3-hydroxypropylacrylate)-glycidylmethacrylate-methylmethacrylate], wherein R^(a), R^(c) and R^(d) are each methyl, R^(b) is hydrogen, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 3 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 9. The compound of claim 1 which is poly[9-anthracenemethylimineethylmethacrylate-(4-hydroxybutylacrylate)-glycidylmethacrylate-methylmethacrylate], wherein R^(a), R^(c) and R^(d) are each methyl, R^(b) is hydrogen, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 4 and 1, respectively, and, w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 10. The compound of claim 1 which is poly[9-anthracenemethylimineethylmethacrylate-(2-hydroxyethylacrylate)-glycidylacrylate-methylmethacrylate], wherein R^(a) and R^(d) are each methyl, R^(b) and R^(c) are each hydrogen, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 2 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 11. The compound of claim 1 which is poly[9-anthracenemethylimineethylmethacrylate-(3-hydroxypropylacrylate)-glycidylacrylate-methylmethacrylate], wherein R^(a) and R^(d) are each methyl, R^(b) and R^(c) are each hydrogen, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 3 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 12. The compound of claim 1 which is poly[9-anthracenemethylimineethylmethacrylate-(4-hydroxybutylacrylate)-glycidylacrylate-methylmethacrylate], wherein R^(a) and R^(d) are each methyl, R^(b) and R^(c) are each hydrogen, R_(a) to R_(d) and R₁ to R₉ are each hydrogen, l, m, and n are 2, 4 and 1, respectively, and w, x, y and z are 0.3, 0.3, 0.2, and 0.2, respectively.
 13. A method for preparing a compound of Formula 1 of claim 1, comprising: reacting 9-anthracenemethyliminealkylacrylate monomer, hydroxyalkylacrylate monomer, glycidylalkylacrylate monomer and methylmethacrylate monomer in a solvent to obtain a product; and polymerizing the product with a polymerization initiator.
 14. The method of claim 13, wherein the solvent is selected from the group consisting of tetrahydrofuran, toluene, benzene, methylethylketone, dioxane and mixtures thereof.
 15. The method of claim 13, wherein the polymerization initiator is selected from the group consisting of 2,2′-azobisisobutyronitrile, acetylperoxide, lauryl peroxide, t-butylperoxide, and mixtures thereof.
 16. The method of claim 13, wherein the polymerization reaction is carried out at a temperature ranging from about 50 to about 90° C.
 17. An anti-reflective coating composition comprising the compound of Formula 1 of claim 1 and a compound of the following Formula 2:

wherein, R₁₀ and R₁₁ are each C₁₋₁₀ alkoxy, and R₁₂ is hydrogen or methyl.
 18. The composition of claim 17 further comprising an anthracene derivative additive selected from the group consisting of anthracene, 9-anthracenemethanol, 9-anthracenecarbonitrile, 9-antracene carboxylic acid, ditranol, 1,2,10-anthracentriol, anthraflavonic acid, 9-anthraldehydeoxime, 9-anthraldehyde, 2-amino-7-methyl-5-oxo-5H-[1]benzo-pyrano[2,3-b]pyridine-3-carbonitrile, 1-aminoanthraquinone, anthraquinone-2-carboxylic acid, 1,5-dihydroxyanthraquinone, anthrone, 9-anthryle trifluoro-methylketone, 9-alkylanthracene derivatives, 9-carboxylanthracene derivatives, 1-carboxylanthracene derivatives and mixtures thereof.
 19. A method for preparing an anti-reflective coating which comprises the steps of: dissolving the compound of Formula 1 of claim 1 and the compound of Formula 2 of claim 17 in an organic solvent to obtain a solution; filtering the solution alone or in combination with an anthracene derivative additive selected from the group consisting of anthracene, 9-anthracenemethanol, 9-anthracenecarbonitrile, 9-antracene carboxylic acid, ditranol, 1,2,10-anthracentriol, anthraflavonic acid, 9-anthraldehydeoxime, 9-anthraldehyde, 2-amino-7-methyl-5-oxo-5H-[1]benzo-pyrano[2,3-b]pyridine-3-carbonitrile, 1-amino-anthraquinone, anthraquinone-2-carboxylic acid, 1,5-dihydroxyanthraquinone, anthrone, 9-anthryle trifluoro-methylketone, 9-alkylanthracene derivatives, 9-carboxylanthracene derivatives, 1-carboxylanthracene derivatives and mixtures thereof to obtain a filtrate; coating the filtrate on a lower layer to obtain a coated layer; and hard-baking the coated layer.
 20. The method of claim 19, wherein the organic solvent is selected from the group consisting of ethyl-3-ethoxypropionate, methyl 3-methoxypropionate, cyclohexanone, and propyleneglycolmethylether acetate and is used in an amount of ranging from about 200 to about 5,000 wt. % based on the total weight of the anti-reflective coating resin used.
 21. The method of claim 19, wherein the hard-baking is carried out at a temperature ranging from about 100 to about 300° C.
 22. A semiconductor device prepared from the anti-reflective coating composition of claim
 17. 23. A semiconductor device prepared from the anti-reflective coating composition of claim
 18. 